EP polyester fabric conveyor belt

Number of views:

1000

EP polyester fabric conveyor belt

Polyester fabric conveyor belts are also called EP belts, whose frameworks are composed of polyester canvas knitted by radial Dacron and weft poly-amide. They are characterized by low radial tensile rate and excellent groove forming ability and good water resistance. Their strength won't be weakened by moisture. Moreover, they won't mould and enjoys high initial modulus.

Retail price

0.0

Yuan

Market price

0.0

Yuan

Number of views:

1000

Product serial number

Category：

EP/NN conveyor belt

Quantity

-

+

Stock:

For more information, please send an email or call our hotline.

+86-576-83010521

seller@kailirubber.com

0.0 $

Inquiry



1

Description

Parameters

Polyester fabric conveyor belts are also called EP belts, whose frameworks are composed of polyester canvas knitted by radial Dacron and weft poly-amide. They are characterized by low radial tensile rate and excellent groove forming ability and good water resistance. Their strength won't be weakened by moisture. Moreover, they won't mould and enjoys high initial modulus.

PRODUCT INTRODUCTION

SPECIFICATION

Specification and technical data of multi-ply polyester conveyor belt

织物类型 Fabric type	织物构造 Fabric structure		织物型号 Fabric specs	胶布厚度 Ply thickness (mm/p)	强度系列(N/mm) Stiength series					覆盖胶厚度(mm) Cover thickness		宽度范围(mm) Width	带长(m) Length
织物类型 Fabric type	经 Warp	纬 weft	织物型号 Fabric specs	胶布厚度 Ply thickness (mm/p)	2层 2Ply	3层 3Ply	4层 4Ply	5层 5Ply	6层 6Ply	上覆盖胶 Upper	下覆盖胶 Lower	宽度范围(mm) Width	带长(m) Length
聚酯 Polyester (EP)	聚酯 Polyester (EP)	锦纶 Polyamine (P)	EP-80	0.60	160	240	320	400	480	1.5-12	0-4.5	400-2500	≤300
			EP-100	0.75	200	300	400	500	600			500-2500
			EP-150	1.00	300	450	600	750	900
			EP-200	1.10	400	600	800	1000	1200
			EP-250	1.25	500	750	1000	1250	1500
			EP-300	1.35	600	900	1200	1500	1800
			EP-350	1.45	-	1050	1400	1750	2100			800-2500
			EP-400	1.55	-	-	1600	2000	2400			800-2500
			EP-450	1.70	-	-	2000	2500	3000			1000-2500

Cover rubber grade DIN 22102

Type	Standard	Tensile Strength min. MPa	Ultimate elongation min. %	Abrasion max. mm	Density g/cm	Basic material	Hardness °Sh	Tenperature range °C
GENERAL PURPOSE BELTS
P	MF/H-13*	10	300	250	1.26	SBR	60±5	-45 to +60
N	DIN 22102 Z ISO 10247 L BS10247 D	17	400	150	1.13	SBR	60±5	-45 to +60
W	DIN 22102 W ISO 10247 D	18	400	90	1.12	NR/BR	60±5	-60 to +60
Y	DIN 22102 Y	20	400	150	1.13	IR/SBR	60±5	-45 to +60
X	DIN 22102 X ISO 10247 H BS 490 M 24	25	450	120	1.11	NR	60±5	-45 to +60
Z	DIN 22102 Z	15	350	250	1.15	SBR	60±5	-20 to +60
HEAT RESISTANT BELTS
HEAT	ISO 4195	15	400	150	1.13	SBR	60±5	-20 to +150
HHEAT	MF/H-T1*	10	400	200	1.07	EPDM	60±5	-20 to +125
HHEAT	MF/H-T2*	10	400	200	1.07	EPDM	60±5	-20 to +150
HHEAT	MF/H-T3*	10	400	200	1.07	EPDM	60±5	-20 to +200
FIRE RESISTANT BELTS
K	DIN 22102 K ISO 433 K	15	400	150	1.30	NR/BR	60±5	-30 to +60
S	DIN 22102 S ISO 433 S	15	400	150	1.30	NR/BR	60±5	-30 to +60
VT	DIN 22109/ 4 vt	15	350	200	1.29	MBR/ NBR- PVC	60±5	-30 to +60
OIL RESISTANT BELTS
MOR³	DIN 22102 G	15	450	200	1.12	MBR/ SBR-	60±5	-30 to +60
PITCH	MF/H-6*	15	450	200	1.11	MBR/ /BR/IR	55±5	-60 to +60
OR	DIN 22102 G	12	300	200	1.25	MBR	60±5	-20 to +100

Adhesion and elongation of the belt

带芯材料 Belt carcass	粘合强度 Adhesive strength			延伸性能Elongation
	布层间 Between plies	覆盖与布层间(N/mm)Between rubber and carcass		全厚度纵向拉断伸长率 Longitudinal elongation at break	全厚度纵向参考力伸长率 Longitudinal elongation at reference %≤
		覆盖层厚度≤1.5mm Rubber thickness ≤1.5mm	覆盖层厚度>1.5 Rubber thickness >1.5	%≥
聚酯帆布 EP canvas	≥4.50	≥3.15	≥3.50	10	1.5

For detailed patterns, please see "Chevron conveyor belt"

Scan the QR code to read on your phone

RELATED PRODUCTS

Explore Our Product Lineup

Coal feeder conveyor belt

Abrasion resistant conveyor belt

EP polyester fabric conveyor belt

Polyester fabric conveyor belts are also called EP belts, whose frameworks are composed of polyester canvas knitted by radial Dacron and weft poly-amide. They are characterized by low radial tensile rate and excellent groove forming ability and good water resistance. Their strength won't be weakened by moisture. Moreover, they won't mould and enjoys high initial modulus.